solidification cracking

基本解释

Solidification cracking is a critical problem during the welding of nickel-based corrosion-resistance materials.
镍基耐蚀材料的焊接结晶裂纹是该类材料焊接性研究中的关键性问题。
Heater leak occurs by direct reason of the stress corrosion cracking, while by other reasons of solidification cracking, small fusion depth of welding joint and non…
应力腐蚀裂纹是造成加热器泄漏的直接原因，结晶裂纹、焊缝熔深小及坡口底部未熔透也是加热器泄漏的原因。
The solidification analysis on shot cracking proved that hot cracking was influenced by the cooling rate of alloy under uncompensated stage of solidification process.
理论分析认为，合金在不可补缩区的冷却速率变化是改变合金热裂程度的重要因素。