slow strain rate test

基本解释

Stress corrosion cracking of an X60 pipeline steel in soil containing water has been investigated using slow strain rate test.
用光滑试样慢应变速率拉伸法研究了X60管线钢在含水土壤中的应力腐蚀。
On the base of above appoints, the slow strain rate test was used to study the effect of prestraining on the SCC susceptibility of X70 pipeline steel in simulate soil media.
基于以上的观点，本文采用慢应变速率实验方法探讨了预形变对X70管线钢在模拟土壤介质中应力腐蚀敏感性的影响。
Stress corrosion crack (SCC) susceptibility of titanium alloy TA7 in methanol and hydrochloric acid-methanol solutions was studied by slow strain rate tensile test (SSRT), SEM and optical photography.
采用慢应变速率试验，辅以扫描电镜、金相观察等分析测试技术，研究了钛合金TA7在甲醇、盐酸-甲醇溶液中的应力腐蚀敏感性。